Adhesive lined, heat shrink insulating caps specifically designed to insulate, seal and protect end or stub splices in wiring harness and electronic assemblies.
Code |
Size (mm) |
Standard Length(mm) |
Expanded |
|
Recoverd |
|
|
---|---|---|---|---|---|---|---|
Internal Diameter Min(mm) |
Internal Diameter Max(mm) |
Outer Layer Thickness (mm) |
Adhesive Thickness (mm) |
Total Wall Thickness (mm) |
|||
3.2 |
22 |
≥5.72 |
≤1.27 |
≥0.64 |
≥0.56 |
≥1.20 |
|
4.8 |
25.4 |
≥7.44 |
≤1.65 |
≥0.76 |
≥0.76 |
≥1.52 |
|
6.4 |
28.4 |
≥10.85 |
≤2.41 |
≥0.89 |
≥1.37 |
≥1.91 |
Property |
Test Method |
Standard |
Typical Performance |
---|---|---|---|
Tensile Strengtn(MPa) |
ASTM D2671 |
≥10.4 |
11.5 |
Elongation(%) |
ASTM D2671 |
≥300 |
450 |
Tensile Strengtn after aging (MPa) |
UL224 158℃X168hr |
≥7.3 |
8.5 |
Elongation after aging(%) |
Ul224 158℃X168hr |
≥200 |
350 |
Dieletric strength(kV/mm) |
IEC 60243 |
≥15 |
17.5 |
Volume resistivity(Ω.cm) |
IEC 60093 |
≥1X101 4 |
2.5X101 4 |
Semi-rigid, adhesive lined, heat shrink insulating caps specifically designed to insulate, seal and protect end or stub splices under extreme operating conditions
Code |
Size (mm) |
Standard Length (mm) |
Expanded |
Recoverd |
|||
---|---|---|---|---|---|---|---|
Internal Thickness Min(mm) |
Internal Diameter Man(mm) |
Outer Layer Thickness (mm) |
Adhesive Thickness (mm) |
Total Wall Thickness (mm) |
|||
CAPS |
3.2 |
22 |
3.2 |
0.80 |
0.64 |
0.56 |
1.20 |
CAPS |
4.8 |
25.4 |
4.8 |
1.30 |
0.76 |
0.76 |
1.52 |
CAPS |
6.4 |
28.4 |
6.4 |
1.52 |
1.00 |
0.91 |
19.10 |
CAPS |
9.5 |
31.8 |
9.5 |
2.00 |
1.08 |
1.00 |
2.08 |
CAPS |
12.7 |
38.1 |
12.7 |
2.41 |
1.30 |
1.24 |
2.54 |
Property |
Test Method |
Standard |
Typical Performance |
---|---|---|---|
Tensile Strengtn(MPa) |
ASTM D2671 |
≥10.4 |
11.5 |
Elongation(%) |
ASTM D2671 |
≥300 |
450 |
Tensile Strengtn after aging (MPa) |
UL224 158℃X168hr |
≥7.3 |
8.5 |
Elongation after aging(%) |
UL224 158℃X168hr |
≥200 |
350 |
Dieletric strength(kV/mm) |
IEC 60243 |
≥15 |
17.5 |
Volume resistivity(Ω.cm) |
IEC 60093 |
≥1X101 4 |
2.5X101 4 |
Crystal clear, semi-rigid, adhesive lined tubing with integral solderless splice connector
Code |
Size |
Tube Diameter |
Color |
Standard Package |
|||
---|---|---|---|---|---|---|---|
AWG |
mm2 |
Expanded Min(mm) |
Recovered Max(mm) |
Length (mm) |
|||
4.8 |
1.2 |
35.0 |
red |
1000pc/bag |
|||
5.5 |
1.4 |
35.0 |
blue |
1000pc/bag |
|||
6.5 |
1.5 |
42.0 |
yellow |
500pc/bag |
Property |
Test Method |
Standard |
Typical Performance |
---|---|---|---|
Tensile Strengtn(MPa) |
ASTM D2671 |
≥14 |
16 |
Elongation(%) |
ASTM D2671 |
≥ 300 |
450 |
Tensile Strengtn after aging (MPa) |
UL224 158℃X168hr |
≥7.3 |
15 |
Elongation after aging(%) |
Ul224 158℃X168hr |
≥200 |
350 |
Dieletric strength(kV/mm) |
IEC 60243 |
≥15 |
17.5 |
Volume resistivity(Ω.cm) |
IEC 60093 |
≥1X101 4 |
2.5X101 4 |
Property |
Test Method |
Standard |
---|---|---|
Water Absorption |
ASTM D570 |
<0.5% |
Sofening Point(℃) |
ASTM E28 |
95±5 |
Strength of pearing(PE) |
ASTM D 1000 |
120N/25mm |
Strength of pearing(AL) |
ASTM D 1000 |
80N/25mm |
Heat shrink end caps are a simple yet effective method for sealing cable ends, pipe, conduit or other similar objects. Typical Applications Watertight sealing of cable ends and pipe conduit Standards Rated for 600/1000V
Expanded Length (Nom) |
Expanded |
Recoverd |
General Use Diameter |
Cable Range |
||||||
---|---|---|---|---|---|---|---|---|---|---|
InternalDiameter Min |
InternalDiameter Max-d |
Wall Thickness Nom-W |
||||||||
mm |
IN |
mm |
IN |
mm |
IN |
mm |
IN |
mm |
IN |
AWG/MCM |
50.80 |
2.00 |
10.20 |
0.40 |
3.80 |
0.15 |
2.00 |
0.080 |
0.18-0.34 |
||
63.50 |
2.50 |
19.10 |
0.75 |
5.60 |
0.22 |
2.00 |
0.080 |
0.24-0.65 |
||
76.20 |
3.00 |
27.90 |
1.10 |
10.20 |
0.40 |
2.40 |
0.095 |
|||
76.20 |
3.00 |
33.00 |
1.30 |
10.20 |
0.40 |
2.40 |
0.095 |
|||
88.90 |
3.50 |
38.10 |
1.50 |
12.70 |
0.50 |
2.40 |
0.095 |
|||
88.90 |
3.50 |
43.20 |
1.70 |
12.70 |
0.50 |
2.50 |
0.100 |
|||
88.90 |
3.50 |
52.10 |
2.05 |
19.00 |
0.75 |
2.50 |
0.100 |
|||
101.60 |
4.00 |
69.80 |
2.75 |
25.40 |
1.00 |
2.50 |
0.100 |
1.2-2.5 |
||
114.30 |
4.50 |
88.90 |
3.50 |
30.00 |
1.18 |
2.50 |
0.100 |
1.3-3.3 |
-- |
|
139.70 |
5.50 |
119.40 |
4.70 |
39.90 |
1.57 |
2.70 |
0.105 |
1.6-4.5 |
-- |
Property |
Test Method |
Standard |
Typical Performance |
---|---|---|---|
Tensile Strengtn(MPa) |
ASTM D2671 |
≥10.4 |
11.5 |
Elongation(%) |
ASTM D2671 |
≥300 |
450 |
Tensile Strengtn after aging (MPa) |
UL224 158 X168hr |
≥7.3 |
8.5 |
Elongation after aging(%) |
UL224 158 X168hr |
≥200 |
350 |
Dieletric strength(kV/mm) |
IEC 60243 |
≥15 |
17.5 |
Volume resistivity(Ω.cm) |
IEC 60093 |
≥1X101 4 |
2.5X101 4 |
Property |
Test Method |
Standard |
---|---|---|
Water Absorption |
ASTM D570 |
≤0.2% |
Sofening Point(℃) |
ASTM E28 |
90±5 |
Strength of pearing(PE) |
ASTM D 1000 |
120N/25mm |
Strength of pearing(AL) |
ASTM D 1000 |
80N/25mm |